http://dspace.bsu.edu.ru/handle/123456789/41238| Название: | Degradation of the creep resistance of a Re-containing 10% Cr steel upon creep testing at low applied stress |
| Авторы: | Fedoseeva, A. E. Nikitin, I. S. Fedoseev, A. E. Kaibyshev, R. O. |
| Ключевые слова: | technique metal science steels 10% Cr steel creep resistance creep testing low applied stresses Laves phase |
| Дата публикации: | 2021 |
| Библиографическое описание: | Degradation of the creep resistance of a Re-containing 10% Cr steel upon creep testing at low applied stress / A.E. Fedoseeva [et al.] // IOP Conference Series: Materials Science and Engineering. - 2021. - Vol.1014.-Art. 012012. - (Synthesis, structure and properties of high entropy materials : Annual School of Young Scientists 2020, Belgorod, Russia, 14-16 October 2020). - Doi: 10.1088/1757-899X/1014/1/012012. - URL: https://iopscience.iop.org/article/10.1088/1757-899X/1014/1/012012/pdf |
| Краткий осмотр (реферат): | New Re-containing steel is a promising material for steam blades of fossil power plants worked at ultra-supercritical parameters of the steam. This steel was subjected to creep testing at 650°C under the applied stresses ranging from 200 to 100 MPa. The steel exhibits excellent creep resistance at high applied stresses; the time to rupture comprises 10,987 hours after the creep test at 650°C/140 MPa |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/41238 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |