http://dspace.bsu.edu.ru/handle/123456789/36874| Title: | Effect of tungsten on creep behavior of 9%cr–3%co martensitic steels |
| Authors: | Fedoseeva, A. Dudova, N. Kaibyshev, R. Belyakov, A. |
| Keywords: | metals creep martensitic steels precipitation electron microscopy |
| Issue Date: | 2017 |
| Citation: | Effect of tungsten on creep behavior of 9%cr–3%co martensitic steels / A. Fedoseeva, N. Dudova, R. Kaibyshev, A. Belyakov // Metals. - 2017. - Vol.7, №12. - Art.573. - URL: https://www.mdpi.com/2075-4701/7/12/573. |
| Abstract: | The effect of increasing tungsten content from 2 to 3 wt % on the creep rupture strength of a 3 wt % Co-modified P92-type steel was studied. Creep tests were carried out at a temperature of 650 °C under applied stresses ranging from 100 to 220 MPa with a step of 20 MPa. It was found that an increase in W content from 2 to 3 wt % resulted in a +15% and +14% increase in the creep rupture strength in the short-term region (up to 103 h) and long-term one (up to 104 h), respectively |
| URI: | http://dspace.bsu.edu.ru/handle/123456789/36874 |
| Appears in Collections: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| File | Description | Size | Format | |
|---|---|---|---|---|
| Effect_of_tungsten_on_creep_behavior_of_.pdf | 4.72 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.