| dc.contributor.author | Fedoseeva, A. | - |
| dc.contributor.author | Dudova, N. | - |
| dc.contributor.author | Kaibyshev, R. | - |
| dc.contributor.author | Belyakov, A. | - |
| dc.date.accessioned | 2021-01-15T12:25:31Z | - |
| dc.date.available | 2021-01-15T12:25:31Z | - |
| dc.date.issued | 2017 | - |
| dc.identifier.citation | Effect of tungsten on creep behavior of 9%cr–3%co martensitic steels / A. Fedoseeva, N. Dudova, R. Kaibyshev, A. Belyakov // Metals. - 2017. - Vol.7, №12. - Art.573. - URL: https://www.mdpi.com/2075-4701/7/12/573. | - |
| dc.identifier.uri | http://dspace.bsu.edu.ru/handle/123456789/36874 | - |
| dc.description.abstract | The effect of increasing tungsten content from 2 to 3 wt % on the creep rupture strength of a 3 wt % Co-modified P92-type steel was studied. Creep tests were carried out at a temperature of 650 °C under applied stresses ranging from 100 to 220 MPa with a step of 20 MPa. It was found that an increase in W content from 2 to 3 wt % resulted in a +15% and +14% increase in the creep rupture strength in the short-term region (up to 103 h) and long-term one (up to 104 h), respectively | - |
| dc.language.iso | en | - |
| dc.rights | 2-s2.0-85038420675 | - |
| dc.subject | metals | - |
| dc.subject | creep | - |
| dc.subject | martensitic steels | - |
| dc.subject | precipitation | - |
| dc.subject | electron microscopy | - |
| dc.title | Effect of tungsten on creep behavior of 9%cr–3%co martensitic steels | - |
| dc.type | Article | - |
| dc.identifier.citationpublication | Metals | - |
| dc.identifier.citationnumber | 12 | - |
| dc.identifier.citationvolume | 7 | - |